http://join2-wiki.gsi.de/foswiki/pub/Main/Artwork/join2_logo100x88.png Hot forging wire and arc additive manufacturing (HF-WAAM)

Duarte, V. R. (Corresponding author) ; Rodrigues, T. A.Extern* ; Schell, N.HZG* ; Miranda, R. M. ; Oliveira, J. P.Extern* ; Santos, T. G.

2020
Elsevier Amsterdam [u.a.]

This record in other databases:      

Please use a persistent id in citations: doi:10.1016/j.addma.2020.101193  doi:10.3204/PUBDB-2020-04680

Abstract: In this study, we propose a new variant of wire and arc additive manufacturing (WAAM) based on hot forging. During WAAM, the material is locally forged immediately after deposition, and in-situ viscoplastic deformation occurs at high temperatures. In the subsequent layer deposition, recrystallization of the previous solidification structure occurs that refines the microstructure. Because of its similarity with hot forging, this variant was named hot forging wire and arc additive manufacturing (HF-WAAM). A customized WAAM torch was developed, manufactured, and tested in the production of samples of AISI316L stainless steel. Forging forces of 17 N and 55 N were applied to plastically deform the material. The results showed that this new variant refines the solidification microstructure and reduce texture effects, as determined via high energy synchrotron X-ray diffraction experiments, without interrupting the additive manufacturing process. Mechanical characterization was performed and improvements on both yield strength and ultimate tensile strength were achieved. Furthermore, it was observed that HF-WAAM significantly affects porosity; pores formed during the process were closed by the hot forging process. Because deformation occurs at high temperatures, the forces involved are small, and the WAAM equipment does not have specific requirements with respect to stiffness, thereby allowing the incorporation of this new variant into conventional moving equipment such as multi-axis robots or 3-axis table used in WAAM.

---

Contributing Institute(s):

1. DOOR-User (DOOR ; HAS-User)
2. Zentrum für Material- und Küstenforschung (HZG)

Research Program(s):

1. 6G3 - PETRA III (POF3-622) (POF3-622)
2. CALIPSOplus - Convenient Access to Light Sources Open to Innovation, Science and to the World (730872) (730872)

Experiment(s):

1. PETRA Beamline P07 (PETRA III)

Appears in the scientific report 2020

---

Database coverage:
; ; ; Clarivate Analytics Master Journal List ; Current Contents - Engineering, Computing and Technology ; Essential Science Indicators ; IF >= 5 ; JCR ; SCOPUS ; Science Citation Index Expanded ; Web of Science Core Collection

---