http://join2-wiki.gsi.de/foswiki/pub/Main/Artwork/join2_logo100x88.png Synthesis of metal-intermetallic laminate (MIL) composites with modified Al$_3$Ti structure and in situ synchrotron X-ray diffraction analysis of sintering process

Lazurenko, D. (Corresponding author)Extern* ; Bataev, I.Extern* ; Stark, A.Extern* ; Pyczak, F.Extern*

2018
Elsevier Science Amsterdam [u.a.]

This record in other databases:      

Please use a persistent id in citations: doi:10.1016/j.matdes.2018.04.038

Abstract: Al$_3$Ti-based alloys attract exceptional attention due to their high specific mechanical properties. However, their application is still insufficient due to their low ductility and fracture toughness. Several approaches were previously proposed to address these problems. The first one is stabilization of the cubic modification of titanium trialuminide by alloying. Another approach consists in fabricating metal-intermetallic laminated composites (MIL). In this study, we combined both methods to synthesize the first MIL composite with cubic Al$_3$Ti interlayers. Copper additions were used to stabilize the cubic modification of Al$_3$Ti and produce a novel Ti-Al$_5$CuTi$_2$ MIL composite. First mechanical characterization by indentation tests showed that the binary Al$_3$Ti intermetallic tended to crack at a load of 0.2 kg while the fracture was not observed in the Al$_5$CuTi$_2$ layers at least at a load of 1 kg. These results are an indirect evidence of a higher ductility and fracture toughness of the composite with cubic Al$_3$Ti compared to tetragonal one. The sequence of the phase transformations in the Al-Ti-Cu system was studied using in situ synchrotron X-ray radiation diffraction. The formation of Al$_5$CuTi$_2$ occurred via several intermediate stages including eutectic melting of Al and Cu and the formation of binary AlCu and Al$_3$Ti compounds.

Note: © Elsevier Ltd.; Post referee fulltext in progress; Embargo 12 months from publication

---

Contributing Institute(s):

1. DOOR-User (DOOR)
2. Zentrum für Material- und Küstenforschung (HZG)

Research Program(s):

1. 6G3 - PETRA III (POF3-622) (POF3-622)
2. FS-Proposal: I-20170107 (I-20170107) (I-20170107)

Experiment(s):

1. PETRA Beamline P07 (PETRA III)

Appears in the scientific report 2018

---

Database coverage:
; Current Contents - Engineering, Computing and Technology ; Ebsco Academic Search ; IF < 5 ; JCR ; SCOPUS ; Science Citation Index Expanded ; Thomson Reuters Master Journal List ; Web of Science Core Collection

---