TI  - Characterization of Native Oxide and Passive Film on Austenite/Ferrite Phases of Duplex Stainless Steel Using Synchrotron HAXPEEM
JO  - Journal of the Electrochemical Society
VL  - 166
IS  - 11
SN  - 1945-7111
CY  - Pennington, NJ
PB  - Electrochemical Soc.
M1  - PUBDB-2019-02412
SP  - C3336 - C3340
PY  - 2019
AB  - A new measurement protocol was used for microscopic chemical analysis of surface oxide films with lateral resolution of 1 μm.The native air-formed oxide and an anodic passive film on austenite and ferrite phases of a 25Cr-7Ni super duplex stainless steelwere investigated using synchrotron hard X-ray photoemission electron microscopy (HAXPEEM). Pre-deposited Pt-markers, incombination with electron backscattering diffraction mapping (EBSD), allowed analysis of the native oxide on individual grains ofthe two phases and the passive film formed on the same area after electrochemical polarization of the sample. The results showeda certain difference in the composition of the surface films between the two phases. For the grains with (001) crystallographicface // sample surface, the native oxide film on the ferrite contained more Cr oxide than the austenite. Anodic polarization up to1000 mV/<sub>Ag/AgCl</sub> in 1M NaCl solution at room temperature resulted in a growth of the Cr- and Fe-oxides, diminish of Cr-hydroxide,and an increased proportion of Fe<sup>3+</sup> species.