@ARTICLE{Ostroushko:205959,
      author       = {Ostroushko, Dmytro and Mazancová, Eva and Saksl, Karel and
                      Halgaš, Radoslav},
      title        = {{M}echanical and {P}hase {A}nalysis of {B}onding {A}rea
                      {E}xplosively {W}elded {T}i-{C}r/{N}i {S}teel in
                      as-{R}eceived {S}tate and after {H}eat {T}reatment {U}sing
                      {S}ynchrotron ({BW}-5)},
      journal      = {Materials science forum},
      volume       = {782},
      issn         = {1662-9752},
      address      = {Uetikon},
      publisher    = {Trans Tech Publ.},
      reportid     = {PUBDB-2015-00492},
      pages        = {155 - 160},
      year         = {2014},
      abstract     = {Surface coatings protection is one of the most important
                      processes ensuring efficient and economic use of basic
                      materials, mostly of lower-quality. At interface of clad and
                      basic material intermetallic phases are formed, representing
                      quite different matrix with dissimilar properties unlike the
                      welded materials. One type of surface coating is explosive
                      bonding which belongs to group of pressure welding. The work
                      is focused on some mechanical properties, micro-and
                      nanohardness controlled by AFM and interface shape line, in
                      homogeneities in vicinity of the wave joint both in basic
                      material and in vicinity of the Ti and Cr/Ni stainless steel
                      matrix weld line. Investigated weld was both in as-received
                      state and after heat treatment carried out at 600°C/90
                      minutes/air. Phases has been identified X-ray diffraction
                      performed BW-5 beamline applying synchrotron radiation, and
                      Tiα, Fe-fcc and Fe-bcc were detected at interface area,
                      whereas intermetallic phases were not revealed.},
      month         = {Apr},
      date          = {2013-04-23},
      organization  = {15th International Symposium on
                       Metallography, Stara Lesna (Slovakia),
                       23 Apr 2013 - 26 Apr 2013},
      cin          = {DOOR},
      ddc          = {670},
      cid          = {I:(DE-H253)HAS-User-20120731},
      pnm          = {DORIS Beamline BW5 (POF2-54G13)},
      pid          = {G:(DE-H253)POF2-BW5-20130405},
      experiment   = {EXP:(DE-H253)D-BW5-20150101},
      typ          = {PUB:(DE-HGF)16},
      UT           = {WOS:000338978600026},
      doi          = {10.4028/www.scientific.net/MSF.782.155},
      url          = {https://bib-pubdb1.desy.de/record/205959},
}