Journal Article

PUBDB-2025-01035

http://join2-wiki.gsi.de/foswiki/pub/Main/Artwork/join2_logo100x88.png Process development and application of hot forging arc-based additive manufacturing on Haynes® 282 for microstructural and mechanical improvements

Felice, I. O. (Corresponding author) ; Marçal, P. R. ; Shen, J.Extern* ; Pizano, L. F. L. ; Xiong, W. ; Schell, N.HZG*Hereon* ; Santos, T. G. ; Oliveira, J. P.Extern*

2025
Elsevier Lausanne

This record in other databases:    

Please use a persistent id in citations: doi:10.1016/j.jallcom.2025.179643  doi:10.3204/PUBDB-2025-01035

Abstract: Haynes® 282, a nickel-based superalloy, is renowned for its exceptional strength, thermal stability, and resistanceto oxidation and creep. While directed energy deposition arc-based additive manufacturing of this alloy hasbeen explored, the formation of large columnar grains and high texture leading to anisotropy and suboptimalmechanical performance remains a significant challenge. This study introduces an interlayer in-situ mechanicaldeformation approach, known as hot forging, to address these issues. The hot forging process, applied at hightemperatures, aims to refine grain structure, reduce porosity, and enhance mechanical properties. The dynamicanalysis of the process using a high-speed camera imaging allowed to calculate a forging force exceeding 1000 N.Two single-bead multi-layered walls were fabricated, one with hot forging and one without. Results demonstrateda 22 % reduction in porosity upon hot forging. Electron backscatter diffraction analysis indicated that thehot forged sample has less texture, and the average grain size decreased from 1746 to 1262 μm and from 1053 to696 μm in the top and middle wall regions, respectively. Synchrotron X-ray diffraction revealed a small variationin phase composition and confirmed that hot forging promotes refined grain structures with less texture. Theultimate tensile strength in the horizontal direction improved by 8 % with hot forging, while elongationdecreased by 30 %. Electrical conductivity and microhardness measurements were similar for both processes.The findings confirm the efficacy of in-situ hot forging in enhancing microstructure and mechanical performance,highlighting its potential for high-cost and low-machinability materials in arc-based additive manufacturing.

---

Contributing Institute(s):

1. Helmholtz-Zentrum Hereon (Hereon)
2. DOOR-User (DOOR ; HAS-User)

Research Program(s):

1. 6G3 - PETRA III (DESY) (POF4-6G3) (POF4-6G3)

Experiment(s):

1. PETRA Beamline P07 (PETRA III)

Appears in the scientific report 2025

---

Database coverage:
; ; ; Clarivate Analytics Master Journal List ; Current Contents - Physical, Chemical and Earth Sciences ; Ebsco Academic Search ; Essential Science Indicators ; IF >= 5 ; JCR ; SCOPUS ; Science Citation Index Expanded ; Web of Science Core Collection

---